Publication Characterization and Optimization of Parylene-C deposition process using SCS Parylene coater(2019-01-15) Hastings, Hannah; Johnston, Eric D; Kim, GyuseokParylene-C has been deposited on bare Si wafers by physical vapor deposition using the SCS Coating Systems. Results show a 12 µm thick Parylene-C film with 10 g of dimer and negligible thickness variation across a wafer. We find a positive linear relationship between film thickness and mass of dimer at a range of 1 g to 18 g. However, the Al boat for dimer was burnt with 18 g of dimer, suggesting multiple depositions with 1 g to 10 g of dimer are recommended to achieve the Parylene-C film thicker than 12 µm.